The effect of the molar ratio of chitosan to sodium monochloroacetate (SMCA) on the degree of substitution (DS) and yield of carboxymethyl chitosan (CMCh) synthesized from chitosan isolated from Uzbek silk reeling waste (tivit) was established. The synthesis was carried out under fixed conditions: temperature 70 °C, time 4 h, isopropanol/water ratio 80/20, stirring speed 500 rpm. The molar ratio was varied from 1:1 to 1:4. The maximum degree of substitution (DS=0.69) and CMCh yield (84.2%) were achieved at a ratio of 1:2. Further increase in SMCA excess to 1:3 leads to a slight increase in DS (up to 0.71) with a decrease in yield (to 78.5%). A ratio of 1:4 results in the formation of by products and a decrease in DS. The obtained results make it possible to recommend a molar ratio of 1:2 as optimal for the synthesis of CMCh from tivit.